| Product description : |
Detailed Product Description
Manufacturer experienced,Stable , continuable,environmental
ISO9001,ISO14001,REACH pre-register.Powder,Granular,Masterbatch
TCY-70 Crosslinking agent for CO, ECO, ACM, CIIR and BIIR, and also co-crosslinking for PVC/NBR
Product description
Composition
70 % 70% 2,4,6-trimercapto-s-triazine,
30% ECO rubber binder and dispersing agents
Appearance
Yellow or light green granules
Density,20 oC
Approx. ~ 1.49 g / cm3 (20oC)
Physiological properties : See safety data sheet (MSDS)
Raw material characteristics of TCY:
Melting point
~ 300 oC
Evaporation loss
≤ 0.5%
TCY content
≥ 97%
Sieve residue 63µm
≤ 0.5 %
Ash content
≤ 0.3 %
Use Characteristics Normally, HiDispersion TCY-70 is used as an effective curing agent for the vulcanization of halogen-containing rubbers such as ECO and CO rubber compounds, CIIR and BIIR compounds, and ACM rubber. But also used as co-crosslinking agent for the NBR/PVC blend. The compounds containing HiDispersion TCY-70 are scorch sensible but sustainable. Compounds therefore should be processed not long after mixing. Compounds have to be stored under cool conditions. Depending on the formulation, storage time should not exceed one week. To improve the storage stability it is recommended to combine TCY-70 with retarders, e.g. HiDispersion CTP-80. HiDispersion TCY-70 shows excellent bonding adhesive between metal and rubbers.
Dosage levels
TCY-70
ZDBC-80
CTP-80
MgO-75
ACM
0.7∼2.1
0.6∼1.9
0∼1.2
-
CO, ECO
0.7∼1.4
-
0∼1.2
4.0
CIIR, BIIR
1.4∼2.9
-
-
0.4∼0.7
Applications ECO, CO, ACM, CIIR, BIIR based industrial goods, NBR/PVC rubber articles.
Packing Net 20 kg cartons with plastic inner.
Storage stability In original closed containers under cool and dry conditions max. 1 years.
Handling Consult material safety data sheet (MSDS) for additional handling information.
|